Title: Penetrating compositions for wet removal of friable insulation materials

What is claimed is:

1. A stripping composition useful for removing a friable material comprising a blend of

T I an aqueous silicate solution component comprising:

(a) 5 to 30 weight percent of an aqueous alkali metal silicate selected from potassium silicate or a mixture of potassium silicate and sodium silicate;

(b) 0.01 to 10 weight percent of a cationic or nonionic surfactant;

(c) 70 to 95 weight percent water; and

T II an acrylic polymer dispersion component comprising:

(a) 45 to 65 weight percent of an acrylic polymer latex having a solids content of 40 to 65 weight percent, said acrylic polymer selected from the group consisting of homopolymers and copolymers of lower alkyl esters of acrylic acid or lower alkyl esters of an alpha-lower alkyl acid or mixtures thereof;

(b) 0.01 to 10 weight percent of a reagent that reacts with said alkali silicate;

(c) 35 to 55 weight percent water;

wherein the ratio of T I to T II provides a blended composition having a solids content between 5 and 30 weight percent.

2. The composition according to claim 1, wherein said aqueous metal silicate is potassium silicate.

3. The composition according to claim 1, wherein said aqueous alkali metal silicate comprises 75 to 95 weight percent of aqueous potassium silicate and from about 5 to 25 weight percent sodium silicate.

4. The composition according to claim 1 wherein said acrylic polymer latex has a solids content of 45 to 60 weight percent.

5. The composition according to claim 1, wherein the volume ratio of T I to T II is 1 to 1.

6. The composition according to claim 1 wherein said reagent is selected from the group consisting of the borate, halide, nitrate and phosphate salts of aluminum, antimony, barium, beryllium, cadmium, calcium, chromium, cobalt, copper, lead, magnesium, mercury, silver and zinc.

7. The composition according to claim 6, wherein said reagent is potassium silicofluoride, zinc silicofluoride and hydrated sodium borate.

8. The method of preparing a stripping composition according to claim 1 comprising the steps of

(a) separately preparing said aqueous silicate solution and the acrylic polymer latex component by mixing predetermined ingredients in said range of concentrations;

(b) preparing said predetermined ingredients of said silicate solution by the steps comprising:

(1) adding said cationic or nonionic surfactant to a stirred aqueous alkali metal silicate solution selected from potassium silicate and mixtures of potassium silicate and sodium-silicate;

(2) adding water;

(3) stirring until a homogenous mixture is formed;

(c) preparing said predetermined ingredients of said acrylic polymer latex component comprising:

(1) stirring said acrylic polymer latex and adding water;

(2) adding said reagent that reacts with said alkali metal silicate component to said stirred acrylic latex component;

(3) stirring until a homogeneous mixture is formed;

(d) storing said aqueous silicate component and said acrylic polymer latex component separately before use; and

(e) mixing said aqueous silicate component and said acrylic polymer latex component.

9. The method of claim 8 wherein said silicate component and said acrylic polymer latex component are mixed in a volume ratio of 1 to 1.

10. The method of claim 8 wherein the alkali metal silicate is potassium silicate.

11. The method of claim 8 wherein the alkali metal silicate is a mixture of potassium silicate and sodium silicate.


Other info:


Inventors: Arpin, John (1716 Melville St., Ocean, NJ, 07712)

Application Number: 06/274172
Filing Date: 1981-06-16
Publication_date: 1982-08-31
Assignee: Arpin, John

Primary Class(es): 510/110 510/406, 134/4, 510/421, 510/109, 510/416, 510/400
Other Classes: C11D3/08; C11D3/37; B08B7/00
US Patent Ref:

3879216	April, 1975	Austin	252/160
3994744	November, 1976	Anderle	252/174.24

Other Refs:
Primary Examiner: Silverberg, Sam
Assistant Examiner:
Attorney: Brady, O'Boyle & Gates